| 合金類型 | 合金牌號(hào) | 合金成分 | Mo當(dāng)量 | 熱處理 | σ/MPa | σ/% |
| α+β合金 | TC21 | Ti-6Al-2Sn-3Mo-1Cr-2Zr-2Nb | 5 |
| 1100-1250 | 6-12 |
| Ti-431 | Ti-4Al-3Mo-1V | 3.7 | 淬火+時(shí)效 | 1350 | 3-5 |
| BT14 | Ti-5Al-3Mo-1V | 3.7 | 淬火+時(shí)效 | 1275 | 4-6 |
| Ti-62222s | Ti-6Al-2Sn-2Zr-2Mo-2Cr-0.25Si | 5.3 | 退火 | 1190 | 11.5 |
| 淬火+時(shí)效 | 1330 | 7.5 |
| Ti-6246/TC19 | Ti-6Al-2Sn-4Zr-6Mo | 6.0 | 退火 | 1162 | 10 |
| 淬火+時(shí)效 | 1214 | 13 |
| BT3-1 | Ti-6Al-2.5Mo-1.5Cr-0.5Fe-0.3Si | 6.0 | 退火 | 1105 | 12 |
| 淬火+時(shí)效 | 1270 | 7-12 |
| BT23 | Ti-5Al-45V-2Mo-1Cr-0.6Fe | 8.1 | 退火 | 1150 | 7 |
| 淬火+時(shí)效 | 1460 | ≥5 |
| SP-700/TC24 | Ti-4.5Al-3V-2Mo-2Fe | 8.1 | 退火 | 1007 | 18.4 |
| 淬火+時(shí)效 | 1377 | 12 |
| BT16 | Ti-3Al-4.5V-5Mo | 8.2 | 退火 | 890 | ≥14 |
| 淬火+時(shí)效 | 1100 | 14 |
| 近亞穩(wěn)β合金 | BT22m | Ti-5Al-5Mo-1V-1Cr-1Fe-1.5Sn-2Zr | 9.4 | 退火 | 1200 | ≥6 |
| TB10 | Ti-3Al-5Mo-5V-2Cr | 11.5 |
| 900-1250 | 8-16 |
| βCEZ | Ti-5Al-4Mo-2Cr-1.2Fe-2Sn-4Zr | 9.7 | 淬火+時(shí)效 | 1506 | 13 |
| Ti-17/ TC12 | Ti-5Al-4Mo-4Cr-2Zr | 10.7 | 退火 | 1160 | 10 |
| 淬火+時(shí)效 | 1300 | 13 |
| βⅢ | Ti-11.5Mo-6Zr-4.5Sn | 11.5 | 淬火+時(shí)效 | 1413 | 7 |
| Ti-1023/TB6 | Ti-10V-2Fe-3Al | 11.1 | 淬火+時(shí)效 | 1275 | 7.5 |
| 退火 | 1175 | 12 |
| BT22/ TC18 | Ti-5Al-4.75Mo-4.75V-1Cr-1Fe | 11.8 | 淬火+時(shí)效 | 1475 | 8 |
| 亞穩(wěn)β合金 | BT22 n | Ti-3Al-5V-5Mo-1.2Cr-1.2Fe | 13.0 | 退火 | 1100 | ≥8 |
| TB2 | Ti-3Al-5Mo-5V-8Cr | 22.2 |
| 1100-1250 | 6-12 |
| TB3 | Ti-3.5Al-10Mo-8V-1Fe | 18 |
| 1000-1300 | 11-20 |
| Ti-5553 | Ti-5Al-5Mo-5V-3Cr-0.5Fe | 13.5 |
| 1100-1240 | 6-18 |
| Ti-55531 | Ti-5Al-5Mo-5V-3Cr-1Zr | 13.5 |
| 1100-1240 | 6-18 |
| Ti-1300 | Ti-5Al-4Mo-4V-4Cr-3Zr | 12.8 |
| 1200-1350 | 8-15 |
| Ti-5321 | Ti-5Al-3Mo-3V-2Cr-2Zr-1Nb-1Fe | 12.8 |
| 1100-1200 | 3-26 |
| Ti-2041 | Ti-4Al-20V-1Sn | 14.3 | 淬火+時(shí)效 | 1530 | 6 |
| Ti-15-3/TB5 | Ti-15V-3Al-3Cr-3Sn | 15.7 | 淬火+時(shí)效 | 1475 | 14 |
| β21S/TB8 | Ti-15Mo-3Al-2.7Nb-0.25Si | 15.8 | 淬火+時(shí)效 | 1260 | 4-5 |
| Timet LCB | Ti-6.8Mo-4.5Fe-1.5Al | 15.8 | 淬火+時(shí)效 | 1470 | 5-8 |
| BT35 | Ti-15V-3Cr-3Al-3Sn-1Zr-1Mo | 16.7 | 淬火+時(shí)效 | 1275 | ≥8 |
| Ti-8823 | Ti-8Mo-8V-2Fe-3Al | 17.7 | 淬火+時(shí)效 | 1250 | 7-8 |
| BT32 | Ti-8V-8Mo-1.5Cr-1.5Fe-3Al | 19.2 | 淬火+時(shí)效 | 1250 | ≥8 |
| βC | Ti-8V-6Cr-4Mo-4Zr-3Al | 19.7 | 淬火+時(shí)效 | 1117 | 18 |
| Ti-13-11-3 | Ti-13V-11Cr-3Al | 27.6 | 淬火+時(shí)效 | 1400 | 6-8 |